Mechanical and the effect of oil absorption on tribological properties of carbon-based brake pad material

Authors

  • Oluwatoyin Joseph Gbadeyan Durban University of Technology
  • T. P. Mohan Durban University of Technology, Durban
  • K. Kanny Durban University of Technology, Durban

Keywords:

Brake pad materials, Carbon-based additives, Mechanical properties, Absorption properties, Nanofiller

Abstract

This research focuses on the mechanical and effect of oil absorption on the tribological properties of carbon-based brake pad material (CBP).  Carbon-based materials, including those at a nanosize, are combined for developed brake pad material. The mechanical properties related to wear properties such as compression strength, stiffness, hardness, and absorption properties were determined. The effect of oil absorption on the tribological properties of carbon-based materials was investigated. The obtained properties are compared with that of a ceramic-made brake pad (commercial). The experimental results show that the mechanical and absorption properties of the developed brake pad material varied with the combination and quantity of additives used to develop each brake pad material. CBP material offered higher performance than ceramic-made brake pads. The CBP material showed a higher shear strength of about 110%, 51% enhanced compressive strength, 35% greater modulus, comparative statistical hardness, 98% lesser water intake, and 97% oil absorption rate than ceramic made brake pad. The tribological properties of friction material after soaked in oil proved that absorption properties affect tribological properties of brake pads, which can be attributed to the oil content in the material system. The effect of oil uptakes on wear rate and friction of the commercial brake pad was higher than CBP materials, implying that the loading of carbon-based materials is a viable way to reduce absorption rate, which helps in increasing brake pad performance. The improved properties are suggestive of materials combinations that may be used to develop brake pad materials.

Section
Peer reviewed articles
Published
Jun 4, 2021

How to Cite

Gbadeyan, O. J., Mohan, T. P., & Kanny, . K. (2021). Mechanical and the effect of oil absorption on tribological properties of carbon-based brake pad material. Tribologia - Finnish Journal of Tribology, 38(1−2), 22−34. https://doi.org/10.30678/fjt.98392